| 標準 | 牌號 | 抗拉強度MPa | 屈服強度MPa | 延伸率% | 端面收縮率 % | 備注 |
| 不 小 于 | ||||||
| ASTM JIS DIN ΓOCΓ GB | GR.1 | 240 | 170 | 24 | 30 | |
| 1類 | 270-410 | 165 | 27 | - | ||
| 3.7025 | 290-410 | 180 | 30 | 35 | ||
| BT1-00 | 295 | - | 20 | -50 | ||
| TA0 | 280 | 170 | 24 | 30 | ||
| ASTM JIS DIN ΓOCΓ GB | GR.2 | 345 | 275 | 20 | 30 | |
| 2類 | 340-510 | 215 | 23 | - | ||
| 3.7035 | 390-540 | 250 | 22 | 30 | ||
| BT1-0 | 345 | - | 15 | 40 | ||
| TA1 | 370 | 250 | 20 | 30 | ||
| ASTM JIS DIN ΓOCΓ GB | GR.3 | 450 | 380 | 18 | 30 | |
| 3類 | 480-620 | 345 | 18 | - | ||
| 3.7055 | 460-590 | 320 | 18 | 30 | ||
| - | - | - | - | - | ||
| TA2 | 440 | 320 | 18 | 30 | ||
| ASTM JIS DIN ΓOCΓ GB | GR.4 | 550 | 483 | 15 | 25 | |
| 4類 | 550-750 | 485 | 15 | - | ||
| 3.7065 | 540-740 | 390 | 16 | 25 | ||
| - | - | - | - | - | ||
| TA3 | 540 | 410 | 15 | 25 | ||
| ASTM JIS DIN GB | GR.7 | 345 | 275 | 20 | 30 | |
| 12類 | 340-``510 | 215 | 23 | - | ||
| 3.7235 | 390-540 | 250 | 22 | - | ||
| TA9 | 370` | 250 | 20 | 25 | ||
| ASTM DIN GB | GR.12 | 483 | 345 | 18 | 25 | |
| 3.7105 | 480 | 345 | 18 | - | ||
| TA10 | 485 | 345 | 18 | 25 | ||
| ASTM JIS DIN ΓOCΓ GB | GR.5 | 895 | 828 | 10 | 25 | |
| 60 | 895 | 825 | 10 | 25 | ||
| 3.7165 | 890 | 820 | 10 | 25 | ||
| BT6 | 885 | - | 8 | 20 | ||
| TC4 | 895 | 825 | 10 | 25 | ||
鈦行業微信交流群，歡迎大家加入! 詳情»
各國鈦及其合金機械性能對照表
2019-06-25 07:05 瀏覽:1272 評論:0
IP屬地 陜西
-
搜鈦奇緣
加關注0
微信：w15399213588
點贊 0
舉報
收藏 0
評論 0
分享 105
中國與ASTM鈦材標準對照表
鈦材常用牌號及規格型號 一：鈦板常用規格 厚度㎜寬度㎜長度㎜厚度允許公差㎜ 0.54.0300--10001500--30000.050.22 5.020.0
2019-06-25 3868
各國工業純鈦牌號化學成分對照表
標準牌號化學成分%不大于其他元素FeCNHOAlSi單一總和ASTMJIS DIN ΓOCΓ GBGR.10.200.080.030.0150.18--0.100.401類0.20-0.050.0
2019-06-25 2046
鈦材料國內外相似牌號對照表
國標化學式美標俄標日標TA1工業純鈦GR1BT1-0TP270TA1-1工業純鈦(板換)GR1BT1-100TA2工業純鈦GR2TP340TA3工業純鈦GR3TP450TA4工業純鈦GR4TP5
2019-01-24 3631
材料對照表(鈦及鈦合金)
合金成分中國GB美國UNS日本JIS德國DINTiTA0R50250/GR.11類3.7025TA1R50400/GR.22類3.7035TA2R50550/GR.33類3.7055TA3R50700/GR.4
2016-06-08 1639